High Strength Grade 80 Lifting Alloy Steel Black Link Chain
High Strength Grade 80 Lifting Alloy Steel Black Link Chain
Category
Application
Related Products
Chain Parameter
SCIC Grade 80 (G80) chains for lifting are made as per EN 818-2 standards, with nickel chromium molybdenum manganese alloy steel per DIN 17115 standards; well designed / monitored welding & heat-treatment ensure chains mechanical properties including test force, breaking force, elongation & hardness.
Figure 1: Grade 80 chain link dimensions
Table 1: Grade 80 (G80) chain dimensions, EN 818-2
|
diameter |
pitch |
width |
unit weight |
|||
|
nominal |
tolerance |
p (mm) |
tolerance |
inner W1 |
outer W2 |
|
|
6 |
± 0.24 |
18 |
± 0.5 |
7.8 |
22.2 |
0.8 |
|
7 |
± 0.28 |
21 |
± 0.6 |
9.1 |
25.9 |
1.1 |
|
8 |
± 0.32 |
24 |
± 0.7 |
10.4 |
29.6 |
1.4 |
|
10 |
± 0.4 |
30 |
± 0.9 |
13 |
37 |
2.2 |
|
13 |
± 0.52 |
39 |
± 1.2 |
16.9 |
48.1 |
4.1 |
|
16 |
± 0.64 |
48 |
± 1.4 |
20.8 |
59.2 |
6.2 |
|
18 |
± 0.9 |
54 |
± 1.6 |
23.4 |
66.6 |
8 |
|
19 |
± 1 |
57 |
± 1.7 |
24.7 |
70.3 |
9 |
|
20 |
± 1 |
60 |
± 1.8 |
26 |
74 |
9.9 |
|
22 |
± 1.1 |
66 |
± 2.0 |
28.6 |
81.4 |
12 |
|
23 |
± 1.2 |
69 |
± 2.1 |
29.9 |
85.1 |
13.1 |
|
24 |
± 1.2 |
72 |
± 2.1 |
30 |
84 |
14.5 |
|
25 |
± 1.3 |
75 |
± 2.2 |
32.5 |
92.5 |
15.6 |
|
26 |
± 1.3 |
78 |
± 2.3 |
33.8 |
96.2 |
16.8 |
|
28 |
± 1.4 |
84 |
± 2.5 |
36.4 |
104 |
19.5 |
|
30 |
± 1.5 |
90 |
± 2.7 |
37.5 |
105 |
22.1 |
|
32 |
± 1.6 |
96 |
± 2.9 |
41.6 |
118 |
25.4 |
|
36 |
± 1.8 |
108 |
± 3.2 |
46.8 |
133 |
32.1 |
|
38 |
± 1.9 |
114 |
± 3.4 |
49.4 |
140.6 |
35.8 |
|
40 |
± 2 |
120 |
± 4.0 |
52 |
148 |
39.7 |
|
45 |
± 2.3 |
135 |
± 4.0 |
58.5 |
167 |
52.2 |
|
48 |
± 2.4 |
144 |
± 4.3 |
62.4 |
177.6 |
57.2 |
|
50 |
± 2.6 |
150 |
± 4.5 |
65 |
185 |
62 |
Table 2: Grade 80 (G80) chain mechanical properties, EN 818-2
|
diameter |
working load limit |
manufacturing proof force |
min. breaking force |
|
6 |
1.12 |
28.3 |
45.2 |
|
7 |
1.5 |
38.5 |
61.6 |
|
8 |
2 |
50.3 |
80.4 |
|
10 |
3.15 |
78.5 |
126 |
|
13 |
5.3 |
133 |
212 |
|
16 |
8 |
201 |
322 |
|
18 |
10 |
254 |
407 |
|
19 |
11.2 |
284 |
454 |
|
20 |
12.5 |
314 |
503 |
|
22 |
15 |
380 |
608 |
|
23 |
16 |
415 |
665 |
|
24 |
18 |
452 |
723 |
|
25 |
20 |
491 |
785 |
|
26 |
21.2 |
531 |
850 |
|
28 |
25 |
616 |
985 |
|
30 |
28 |
706 |
1130 |
|
32 |
31.5 |
804 |
1290 |
|
36 |
40 |
1020 |
1630 |
|
38 |
45 |
1130 |
1810 |
|
40 |
50 |
1260 |
2010 |
|
45 |
63 |
1590 |
2540 |
|
48 |
72 |
1800 |
2890 |
|
50 |
78.5 |
1963 |
3140 |
|
notes: total ultimate elongation at breaking force is min. 20%; |
|||
| changes of Working Load Limit in relation to temperature | |
| Temperature (°C) | WLL % |
| -40 to 200 | 100% |
| 200 to 300 | 90% |
| 300 to 400 | 75% |
| over 400 | unacceptable |